Biomaterial for filling and rebuilding of root canals.
Composition:
BIO MTA+ powder: calcium oxide, hydroxyapatite, oxides of: silicon, iron, aluminum, sodium, potassium, bismuth, magnesium, zirconium; calcium phosphate.
BIO MTA+ liquid: Ph. Eur. purified water, calcium catalyst.
Available Packages:
- MINI 3 x 0,14 g BIO MTA+ powder, 1 ml liquid
- MAXI 10 x 0,14 g BIO MTA+ powder, 2 x 1 ml liquid
Properties of Bio MTA:
The product is intended for dental treatment as a material for filling and remineralisation of root canals. When mixed with the BIO MTA+ liquid, the working life is ca. 4 min, and the compound sets completely in ca. 3 h.
The high content of calcium ions remineralises the tooth tissue. The silicon and calcium compounds support tissue regeneration after wall perforation and intracanal resorption. BIO MTA+ contains hydroxyapatite, a natural component of bones, which integrates the compound perfectly into the bone structure.
BIO MTA+ is especially recommended in:
– root canal wall perforation
– intracanal resorption
– filling of the posterior root apex
– direct coating of the pulp
– pulp amputation
– treatment of teeth with interrupted root development.
BIO MTA+ is not suitable as a standalone permanent root canal filling.
Once its two components have been mixed, BIO MTA+ exhibits extremely plastic and cohesive consistence without brittling and stays on the instruments. This facilitates the application BIO MTA+ when compared with the traditional MTA compounds.
Instructions for use:
Cut off the BIO MTA+ liquid pipette tip. Move the entire contents of the BIO MTA+ powder glass vial with 1 to 2 drops of the BIO MTA+ liquid on a mixing plate.
Mix for ca. 30 s until the compound reaches a consistence of soft plasticine (modelling putty). If the compound mix is too thick or too brittle, add one more drop of the BIO MTA+ liquid